Material | 100%virgin HDPE Material |
---|---|
Color | White,black |
Tensile Strength | 23Mpa |
Density | 0.96g/cm³ |
Length | 1-2m |
Material | 100% Virgin HDPE Material |
---|---|
Color | White, Black |
Produce | Extrude |
Tensile Strength | 23Mpa |
Density | 0.96g/cm3 |
Material | 100%virgin HDPE Material |
---|---|
Color | White,black |
Tensile Strength | 23Mpa |
Density | 0.96g/cm³ |
Length | 1-2m |
Material | PVC Material |
---|---|
Color | White, Black, Grey |
Tensile Strength | 52Mpa |
Impact Strength | 5KJ/m2 |
Density | 1.5g/cm3 |
Material | 100%virgin HDPE Material |
---|---|
Color | White,black |
Tensile Strength | 23Mpa |
Density | 0.96g/cm³ |
Length | 1-2m |
Material | 100% Virgin Polyether,polyester |
---|---|
Color | Yellow,brown,black,red |
Akron Abrasion Loss | <0.05cm3/1.61km |
Compression Set | <10%(22h*70°C) |
Working Temperature | Maximum 120°C |
Material | 100% Virgin Polyether, Polyester |
---|---|
Color | Yellow, Brown, Black, Red Etc. |
Akron Abrasion Loss | <0.05cm3/1.61km |
Compression Set | <10%(22h*70°C) |
Working Temperature | Maximum 120°C |
Material | 100% Virgin Polyether,polyester |
---|---|
Color | Yellow,brown,black,red |
Akron Abrasion Loss | <0.05cm3/1.61km |
Compression Set | <10%(22h*70°C) |
Working Temperature | Maximum 120°C |
Material | 100% Virgin PTFE Material |
---|---|
Color | White, Black |
Tensile Strength | 20-30Mpa |
Hardness | 50-60shore D |
Elongation | 200-300% |
Material | 100% Virgin POM Material |
---|---|
Color | White, Black |
Tensile Strength | 62Mpa |
Density | 1.45g/cm3 |
Impact Strength | 80-100KJ/m2 |